Influence of prophylaxis paste treatment on the abrasive wear of surface sealants

Abstract

Objective. To investigate the abrasive wear of surface sealants (Seal&Protect and K-0184 (experimental sealant)) and the influence of pre-treatment with mineral deposit forming prophylaxis pastes (NUPRO Sensodyne and NUPRO) on this wear. Methods. One hundred and eight bovine dentine samples were randomly allocated to nine groups (1–9). Pre-treatment (10 s): groups 1–3: untreated, groups 4–6: NUPRO, groups 7–9: NUPRO Sensodyne. Sealing: groups 1, 4 and 7: unsealed, groups 2, 5 and 8: Seal&Protect, groups 3, 6 and 9: K-0184 (experimental sealer). Samples were then brushed with 12 000 brushing strokes (BS) with toothpaste slurry in an automatic brushing machine (120 BS/min; F = 2.5 N). Surface profiles were recorded at baseline, after pre-treatment and sealing and after each 2000 BS. Results. Total profile change (wear or gain due to pre-treatment, treatment and 12 000 BS): groups 1, 4 and 7 (no surface sealant) showed a not significantly different wear of 18.48 ± 2.63 µm, 24.98 ± 3.02 µm and 21.50 ± 5.47 µm, respectively. Remaining groups (sealed) showed a gain in height with no significant difference among each other. Wear in sealed groups (2, 3, 5, 6, 8 and 9) were not significantly different at all numbers of brushing strokes. Starting with 4000 BS, the wear in unsealed groups (1, 4 and 7) was statistically significantly higher compared to all other groups. Conclusion. Stability and wear resistance of surface sealants are not affected by pre-treatment of dentine with NUPRO Sensodyne. The surface sealants tested provide a stable protective surface layer on dentine, which lasts for at least 12 000 brushing strokes.