Long-term corrosion studies in vitro of gold, cobalt-chromium, and nickel-chromium alloys in contact

Abstract

Specimens of various types of dental casting alloys were stored in phosphate-buffered 0.9% NaCI solution for 35 weeks. Every 7 weeks the solutions were changed and analyzed with regard to elements released from the alloys. The release of Cu from type III gold alloy increased in contact with gold alloys for metallo-ceramic use in a 1:2 area relation. However, when the area relation was reversed, no difference in the amounts of elements released was observed. Crevice corrosion was initiated with one of the Co-Cr alloys in contact with type III gold alloy. The crevice corrosion increased the amounts of Co and Cr released into the solutions. The release of Ni and Cr from the Ni-Cr alloys was prominent. These alloys were very susceptible to crevice corrosion. With one of the Ni-Cr alloys the release of elements increased in contact with type III gold alloy.