Pre-treating dentin with chlorhexadine and CPP-ACP: self-etching and universal adhesive systems

Abstract

Objective: The aim of the present study was to compare the effect of pre-treating dentin with chlorhexidine, at concentrations of 0.2% and 2%, and remineralizing paste containing CPP-ACP (MI Paste – GC) on the bond strength of adhesive systems.

Material and methods: In total, 80 slides of dentin were used. These slides were 2 mm thick and were obtained from bovine incisors. Standard cavities were created using diamond bur number 3131. In the control groups, a Scotchbond Universal Adhesive (SUA) self-etching adhesive system of 3M ESPE and a Clearfil SE Bond (CSE) adhesive system of Kuraray were applied, following the manufacturer’s instructions. In the other groups, dentin was pretreated with chlorhexidine (0.2% and 2%) for 1 min and with MI Paste for 3 min. The cavities were restored with Z350 XT resin (3M ESPE). After 24 h of storage, the push-out test was applied at a speed of 0.5 mm/min.

Results: The different dentin pretreatment techniques did not affect the intra-adhesive bond strength. There was a difference between treatment with MI Paste and chlorhexidine 0.2% in favor of the SUA, with values of 15.22 and 20.25 Mpa, respectively.

Conclusions: The different pretreatment methods did not alter the immediate bond strength to dentin. Differences were only recorded when comparing the adhesives.