Repair bond strength of bulk-fill composites: influence of different primers and direction of debonding stress

Abstract

Background

The purpose of this in vitro study was to evaluate the effect of different adhesion primers on the repair bond strength of bulk-fill resin composite and short-term hydrolytic stability of the repair interface before and after accelerated aging. In addition, direction of debonding stress was examined.

Materials and methods

Bulk-fill substrates were aged in water for 14 days at 37 °C. Smooth resin composite surfaces were prepared for the substrates with a superfine grinding paper (FEPA #500, #1200, #2000). Test specimens were produced by attaching bulk-fill composite to the substrate surfaces, using three different primer/bonding systems. Specimens were aged 24 h at 37 °C in water, or thermal cycled (5–55 °C/5,000 cycles). Subsequently, shear bond strength and micro-tensile bond strength were evaluated. In total there were 60 specimens for the shear bond strength and 60 specimens for the micro-tensile bond strength measurements (30 stored in water 24 h, 30 thermal cycled, n = 10 in each primer/bonding mode).

Results

The mean shear bond strength was 9.1–13.1 MPa after 24 h water storage and 6.9–10.7 MPa after thermal cycling. The mean micro-tensile bond strength was 28.7–45.8 MPa after 24 h water storage and 22.7–37.9 MPa after thermal cycling.

Conclusion

The Ceramic primer (silane containing) seems to perform better than the three-step etch and rinse adhesive or the Composite primer. Shear-type stress had an adverse effect on the repair bond strength of bulk-fill resin composites.